Ertalon® LFX
Brand: 
- Self-lubricating
- Up to 50% reduced friction coefficient
- Excellent resistance to wear
- Cobalt green in colour
Interested in this product?
Cast, internally lubricated polyamide 6 is a self-lubricating material for all purposes.
Specifically designed for parts used in dynamic, high load and lube-free applications (slow movements), this material helps expand the scope of polyamides thanks to its low friction coefficient (reduced up to 50%) and enhanced resistance to wear (up t 10 times greater).
| Properties | ISO standard | Unit of measurement | Value |
| General properties | |||
| Colour | cobalt green | ||
| Density (specific weight) | 1183 | g/cm3 | 1.135 |
| Water absorption | 62 | % | 0.66/1.24 |
| Mechanical properties | |||
| Tensile strain at break* | 527 | % | >50 |
| Tensile strain at yield / at break* | 527 | MPa | 45/- |
| Tensile modulus of elasticity* | 527 | MPa | 1450 |
| Impact strength | 179/1eA | kJ/m2 | 4 |
| (Charpy impact test - notched) | |||
| Ball indentation hardness | 2039-1 | N/mm2 | 145 |
| Rockwell hardness | 2039-2 | -- | M82 |
| Thermal properties | |||
| Melting temperature | 11357-1/-3 | °C | 220 |
| Thermal conductivity at 23 °C | -- | W/mK | 0.28 |
| Coefficient of linear thermal expansion | av. value between 23 °C and 60 °C | m/mk | 80x10-6 |
| Working temperature. continuously 5.000/ 20.000 | -- | °C | +105/+90 |
| Working temperature. for short periods | -- | °C | 165 |
| Min. operating temperature | -- | °C | -20 |
| HB/HB flammability (thickness 3/6 mm) | UL94 | -- | HB/HB |
| Electric properties | |||
| Dielectric strength* | 60243 | kV/mm | 14 |
| Volume resistivity* | 60093 | Ohm/cm | >1012 |
| Surface resistivity* | 60093 | Ohm | >1012 |
| Physiological properties | |||
| Suitable for contact with foodstuffs | 21 CFR (FDA) | -- | NO |
* Values measured on materials in standard balanced weather conditions, i.e. 23 °C and 50% RH.