Duratron® T4301 PAI
Brand: 
- Extremely high maximum operating temperature in air;
- Excellent retention of mechanical resistance, stiffness and creep resistance;
- Very low coefficient of linear thermal expansion, up to +250 °C;
- Excellent behaviour with friction and wear;
- Low intrinsic flammability;
Interested in this product?
The addition of graphite and PTFE gives the unmodified grade of this material greater resistance to wear and a lower friction coefficient while minimising or even fully removing the stick-slip effect during use.
This grade excels in severe service wear applications such as non-lubricated bearings and bushings, seals, bearing cages, and parts for reciprocating compressors.
Specifications
- High maximum operating temperature in air (+250 °C continuously)
- Excellent retention of mechanical strength, stiffness and creep resistance within a wide range of temperatures
- Very low linear thermal expansion coefficient, up to +250 °C
- Excellent behaviour with friction and wear (this is especially true for DURATRON 4301 PAI)
- Low intrinsic flammability
- Extraordinary resistance against high energy radiation
| Properties | ISO / (IEC) standard | Unit of measurement | Value |
| General properties | |||
| Colour | black | ||
| Density | 1183-1 | g/cm3 | 1.45 |
| Water absorption: | |||
| - after 24/96 h immersion in | 62 | mg | 26/48 |
| water at 23 °C | |||
| 62 | % | 0.30/0.55 | |
| - at saturation in air of 23 °C / 50% RH | -- | % | 1.9 |
| - at saturation in water of 23 °C | -- | % | 3.8 |
| Thermal properties | |||
| Melting temperature | 11357-1/-3 | °C | NA |
| Glass transition temperature | 11357-1/-2 | °C | 280 |
| Thermal conductivity at 23 °C | - | W (K.m) | 0.54 |
| Average coefficient of linear thermal expansion: | |||
| - average value between 23 and 100 °C | - | m/(m.K) | 35x10-6 |
| - average value between 23 and 150 °C | - | m/(m.K) | 35x10-6 |
| - average value above 150 °C | - | m((m.K) | 40x10-6 |
| Deflection temperature under load: | |||
| - method A: 1.8 MPa | 75-1/-2 | °C | 280 |
| Max. operating temperature in air: | |||
| - for short periods | - | °C | 270 |
| - continuously: min. 20.000 h | - | °C | 250 |
| Min. operating temperature | -20 | ||
| Flammability: | |||
| - "Oxygen index" | 4589-1/-2 | % | 44 |
| - according to method UL 94 | - | - | V-0/V-0 |
| (1.5/3 mm thickness) | |||
| Mechanical properties at 23 °C | |||
| Tension test | |||
| - Tensile stress at yield / tensile stress at break | 527-1/-2 | MPa | NYP/110 |
| - Tensile strain at break | 527-1/-2 | % | 5 |
| - Tensile modulus of elasticity | 527-1/-2 | MPa | 5500 |
| Compression test | |||
| - Compressive stress at 1% nominal strain | 604 | MPa | 39 |
| - Compressive stress at 2% nominal strain | 604 | MPa | 72 |
| Charpy impact strength - unnotched | 179-1/1eU | kJ/m2 | 45 |
| Charpy impact strength - notched | 179-1/1eA | kJ/m2 | 4 |
| Ball indentation hardness | 2039-1 | N/mm2 | 200 |
| Rockwell hardness | 2039-2 | - | M 106 (E 70) |
| Electrical properties at 23 °C | |||
| Dielectric strength | (60243-1) | kV/mm | -- |
| Volume resistivity | (60093) | Ohm.sq | >1013 |
| Surface resistivity | ANSI/ESD | Ohm.sq | >1013 |
| STM 1111 | |||
| Relative permittivity Â: | 60250 | -- | 6 |
| at 100 Hz | |||
| at 1 MHz | 60250 | -- | 5.4 |
| Dielectric dissipation factor. tan ‰: | 60250 | -- | 0.037 |
| at 100 Hz | |||
| at 1 MHz | 60250 | -- | 0.042 |
| Comparative Tracking Index | 60112 | -- | 175 |
| (CTI) |
Although the information provided in this product data sheet is confirmed by reliable research, POLITECNICA CETAI shall not take any responsibility for the application, processing or use of such information.