PA 66-GF30
Brand: 
- Enhanced mechanical strength
- Enhanced stiffness
- Enhanced dimensional stability
- Excellent wear resistance
- Very good resistance to elevated temperatures
Interested in this product?
Compared to virgin PA 66, this heat stabilised polyamide, modified with 30% fibreglass, shows enhanced mechanical strength, stiffness, dimensional stability, and creep resistance, as well as excellent wear resistance and usability at more elevated temperatures.
| Properties | ISO standard | Unit of measurement | Value |
| General properties | |||
| Colour | black | ||
| Density (specific weight) | 1183 | g/cm3 | 1.29 |
| Water absorption | 62 | % | 0.39/0.74 |
| Mechanical properties | |||
| Tensile strain at break* | 527 | % | 12 |
| Tensile strain at yield / at break* | 527 | MPa | -/75 |
| Tensile modulus of elasticity* | 527 | MPa | 3200 |
| Impact strength | 179/1eA | kJ/m2 | 6 |
| (Charpy impact test - notched) | |||
| Ball indentation hardness | 2039-1 | N/mm2 | 165 |
| Rockwell hardness | 2039-2 | -- | M76 |
| Thermal properties | |||
| Melting temperature | 11357-1/-3 | °C | 255 |
| Thermal conductivity at 23 °C | -- | W/mK | 0.3 |
| Coefficient of linear thermal expansion | av. value between 23 °C and 60 °C | m/mK | 50x10-6 |
| Working temperature. continuously 5.000/20.000 hours | -- | °C | +120/+110 |
| Working temperature. for short periods | -- | °C | 240 |
| Min. operating temperature | -- | °C | -20 |
| HB/HB flammability (thickness 3/6 mm) | UL94 | -- | HB/HB |
| Electric properties | |||
| Dielectric strength* | 60243 | kV/mm | 20 |
| Volume resistivity* | 60093 | Ohm/cm | >1013 |
| Surface resistivity* | 60093 | Ohm | >1012 |
| Physiological properties | |||
| Suitable for contact with foodstuffs | 21CFR (FDA) | -- | NO |
* Values measured on materials in standard balanced weather conditions, i.e. 23 °C and 50% RH.
Although the information provided in this product data sheet is confirmed by reliable research, POLITECNICA CETAI shall not take any responsibility for the application, processing or use of such information.